ABSTRACT

Conclusion:

The material structure of the one-piece hydrophobic surfaced high water content acrylic foldable IOLs, the implantation system and foldable cartridge used are the factors that can potentiate the development of damage in the IOL during implantation. For a problem-free implantation, it should be done carefully and slowly from inserting the IOL into the cartridge until it is placed in the capsule bag.

Results:

The properties of implanted 4,195 IOLs of 4,778 were hydrophobic acrylic (835 SA60AT, 2,438 AAB00, 922 ZCB00). The remaining 583 IOLs were hydrophobic surfaced high water content acrylic (UD 613). Hydrophobic acrylic IOLs with high water content were inserted with a disposable plastic syringe and foldable cartridge, and hydrophobic acrylic IOLs were inserted with a reusable metal syringe and disposable non-foldable cartridge. Of the 11 IOLs whose integrity was impaired during implantation, 8 were hydrophobic surfaced high water content acrylic and 3 were hydrophobic acrylic (p<0.001). There was no statistically significant difference between hydrophobic acrylic lenses (p=0.103).

Materials and Methods:

In this study, medical records of 3,856 patients (4,778 eyes) who underwent phacoemulsification and foldable IOL implantation by cartridge between August 2010 and July 2019 were retrospectively reviewed. The 11 eyes of 11 patients who had undergone IOL removal and reimplantation were noted for IOL damage during implantation. In other eyes, implanted IOL material, injector and cartridge type information were recorded.

Aim:

To evaluate the factors affecting intraocular lens (IOL) integrity during implantation in phacoemulsification surgery.

INTRODUCTION

Intraocular lens (IOL) implantation during the modern phacoemulsification procedure is one of the basic principles of successful cataract surgery. With the introduction of foldable IOLs in modern surgeries, IOL implantation has become possible through a smaller corneal incision. In the historical development process of cataract surgery, many IOL and IOL implantation systems have been developed to increase the success of surgeries. While the IOL is placed in the eye with various injector systems and cartridges, complications requiring IOL replacement may occur. Some of these complications include damage to the lens capsule and zonule or damage to the IOL optic and haptic structure of the IOL during implantation. As a result of not being able to centralize the optic of the IOL, a decrease in visual acuity may occur after surgery. If the IOL optic cannot be centralized as a result of damage to the optic or haptic structure of the IOL, explantation and re-implantation should be performed^1,2.

In this study, we aimed to evaluate the effects of two different injector and cartridge systems used during intraocular implantation of one-piece hydrophobic and hydrophobic surfaced with high water content acrylic, two types of acrylic IOLs with different material properties, on possible IOL damage.

GİRİŞ

Modern fakoemülsifikasyon işlemi sırasında göz içi lens (GİL) implantasyonu başarılı bir cerrahinin temel şartlarından biridir. Katlanabilir GİL’lerin kullanılması ile birlikte, daha küçük korneal kesiden GİL implantasyonu yapılabilir hale gelmiştir. Katarakt cerrahisinin tarihsel gelişiminde ameliyat başarısını artırmak için çok sayıda GİL ve GİL implantasyon sistemleri geliştirilmiştir. GİL çesitli enjektör sistemi ve kartuşlar ile göz içine yerleştirilirken, GİL değişimini gerektirecek komplikasyonlar gelişebilir. GİL implantasyonu sırasında lens kapsülü ve zonülü ya da GİL’nin optik ve haptik yapısının hasar görmesi cerrahi sırasında GİL değişimini gerektiren durumlardandır. GİL optiğinin merkezileştirilememesi, bunun sonucunda görme aksının ortalanamamasının sonucunda ameliyat sonrası görme keskinliğinde azalma meydana gelebilir. GİL’nin optik veya haptik yapısındaki hasarın bir sonucu olarak GİL optiği merkezileştirilemezse, eksplantasyon ve yeniden implantasyon yapılmalıdır^1,2.

Bu çalışmada iki farklı materyal özelliklerine sahip tek parçalı yüksek su içerikli hidrofobik yüzeyli akrilik ve tam hidrofobik akrilik GİL’lerin veya göz içi implantasyonu sırasında kullanılan iki farklı enjektör ve kartuş sisteminin olası GİL hasarına etkilerinin değerlendirilmesi amaçlanmıştır.

MATERIALS AND METHODS

4778 eyes of 3856 patients who underwent phacoemulsification and cartridge-assisted one-piece foldable IOL implantation between August 2010 and July 2019 in Tekirdağ Namık Kemal University Department of Ophthalmology and did not develop complications other than IOL damage during and after the procedure were analyzed retrospectively. The technical characteristics and IOL implantation systems of the IOLs used in all surgeries, the corneal incision length of the eyes containing the IOLs damaged during implantation, the location of the IOL damage, the IOL strength and the implantation order within their group were recorded. This study was approved by Tekirdağ Namık Kemal University Ethics Committee (numbered 2019.09.11.06) and complies with the 2008 Helsinki Declaration. All patients were informed about all stages of the surgical procedure and informed consent was obtained from the patients.

Phacoemulsification and IOL implantation were performed under topical, regional (subtenon and retrobulbar) or general anesthesia. For pupil dilation, phenylephrine 2.5%, cyclopentolate 1% and tropicamide 0.5% drops were applied 3 times with intervals of 5 minutes, 30 minutes before surgery. Topical anesthesia was provided with proparacaine hydrochloride 0.5% drops 4 times at 5 minute-intervals, 20 minutes before the procedure. Regional anesthesia was provided with a mixture of 2 mL 2% lidocaine hydrochloride and 2 mL 0.5% bupivacaine hydrochloride. Povidone iodine was used for surgical area cleaning. For endophthalmitis prophylaxis, 5% povidone iodine was dropped to the fornix; After 3 minutes, it was washed with Ringer’s lactate solution. Two clear corneal side incisions were made with a 20 gauge (G) micro vitreoretinal knife. A cohesive viscoelastic agent (1.4% sodium hyaluronate) was injected into the anterior chamber. The main corneal incision was made with a slit blade (in various incisions between 2.2 mm and 3.2 mm). A flap was created in the anterior capsule with a 27 G cystotome. Continuous curvilinear capsulorhexis was performed with capsulorhexis forceps. After hydrodissection and hydrodelineation, the nucleus was aspirated by shredding with stop and chop and quick chop methods. Lens cortex and residuals were cleaned by bimanual irrigation and aspiration method. All procedures were carried out by experienced three surgeons. Two separate nurses experienced in phacoemulsification procedures inserted the IOL into the cartridge. The cartridge was first wetted with a balanced salt solution, then filled with a cohesive viscoelastic material, and the IOL was made ready for implantation. Hydrophobic acrylic IOLs SA60AT (AcrysoF, Alcon, Fortworth, TX, US), AAB00 (Sensar 1, Abbott Medical Optics, Santa Ana, CA, US) and ZCB00 (Tecnis 1, Abbott Medical Optics, Santa Ana, CA, US) were implanted by disposable non-folded cartridge and reusable metal syringe (Figure 1A); hydrophobic surfaced high water content acrylic IOL UD 613 (Acriva, VSY Biotechnology, İstanbul, Turkey) was implanted by folded disposable cartridges and disposable plastic syringe (Figure 1B)^3,4. After filling the capsule with cohesive viscoelastic, the IOL was placed in the capsule. In order to remove the IOLs that were seen to be damaged during implantation and whose centralization could not be achieved, the IOL incision was made with micro scissors to the center of the IOL optic without expanding the corneal incision. The IOL was rotationally removed from the main corneal incision by holding one side of the incised IOL with colibri forceps. Another IOL of the same feature and diopter was implanted in the capsule. Drops containing topical steroid (prednisolone acetate 1%) and antibiotic (moxifloxacin 0.5%) were started in all patients after surgery. The drops were stopped by gradually reducing the number of doses within two weeks. The IOLs used were divided into 2 groups as hydrophobic acrylic and hydrophobic surfaced high water content acrylic.

Statistical Analysis

The statistical analyses were performed using Statistical Package for the Social Sciences Statistics for Windows, version 24.0 (IBM, Statistical Product and Service Solutions, Inc., Chicago, IL, USA). The difference between groups was evaluated using the chi-square and Fisher’s exact tests. P<0.05 was considered statistically significant.

RESULTS

Of the 4,778 IOLs implanted in the eye after phacoemulsification, 4,195 were hydrophobic one-piece acrylic (835 SA60AT, 922 ZCB00 and 2,438 AAB00) and 583 were hydrophobic surfaced high water content one-piece acrylic UD613 (Acriva) (Table 1). IOL integrity was impaired in 11 patients who were implanted (Table 2). Of the 11 IOLs whose integrity was impaired by damage, 8 were hydrophobic surfaced high water content and 3 were hydrophobic acrylic (p<0.001). When the hydrophobic acrylic IOLs with 3 different designs from two different manufacturers with 8 damaged lenses were compared, the difference was not statistically significant (p=0.103). No complications occurred during the explantation and re-implantation of the IOLs. Of the 8 IOLs with a hydrophobic surfaced high water content acrylic, 7 of them had haptic damage and 1 had optic damage. Haptic damage was observed in 3 of the hydrophobic acrylic IOLs. Two of the hydrophobic surfaced high water content acrylic IOLs had low diopter and were thin. The other 2 IOLs in the same group were damaged during the learning period of the cartridge insertion procedure. The main corneal incision length varied between 2.2 and 3.2 mm (Table 2).

DISCUSSION

The characteristics of the material which the IOL is produced, its optical and haptic design, the implantation system used, improper placement of the IOL in the cartridge, inappropriate placement of the cartridge in the implantation system, inappropriate and inadequate viscoelastic use, and inappropriate cartridges are factors that can adversely affect the IOL integrity during phacoemulsification procedures^5,6.

Foldable acrylic IOLs are the most commonly used materials in phacoemulsification and IOL implantation currently. Although there are one-piece, 3-piece, plate haptic or scleral fixation IOLs in use, we used only one-piece IOLs with haptics in our study. Acrylic IOLs can also be classified as hydrophilic acrylic, hydrophobic surfaced high water content acrylic or hydrophobic acrylic. Hydrophobic IOLs have a water content of less than 1%, while those with hydrophilic and hydrophobic surfaces contain water between 18% and 26%^5,7.

Hydrophilic IOLs consist of a hydroxyethyl methacrylate (polyHEMA) and hydrophilic acrylic monomer. They are soft and their hydrophilic nature provides excellent flexibility. It is possible to be implanted through corneal incisions below two millimeters. It is resistant to damage caused by folding. Because of the high rate of posterior capsule concentration development in hydrophilic IOL implantations, the use of hydrophobic surface and hydrophilic hybrid IOLs has become widespread. These are mostly coated with hydrophobic acrylic on the surface and contain ultrapure acrylate monomer that has a water content of 25%^5,8,9.

Hydrophobic IOLs consist of a series of acrylate and methacrylate copolymers. Rigid polymethylmethacrylate has been transformed into a foldable and durable material. Pull and push force can be applied to hydrophobic IOLs; IOLs can take their old shape in seconds. It can be inserted into the eye through a corneal incision of at least 2.2 mm^5,7,8.

SA60AT, which is a hydrophobic acrylic IOL, has an aspherical and biconvex front surface, while its back surface has a 360° sharp optical edge. Its haptics are “C” shaped and a continuation of optics¹⁰. ZCB00 and AAB00 are other hydrophobic acrylic IOLs; Biconvex, front surface aspherical and posterior surface has an optical square edge 360​°¹¹. The implantation of these IOLs is done with reusable metal injectors and disposable non-folding cartridges designed for these injectors. The IOL is placed in the cartridge groove and the plunger of the metal injector is pushed forward and inserted into the eye. The metal plunger is smaller than the cartridge groove and its rigid structure allows it to push the IOL without compressing the haptics and optics⁴. The resistant nature of the hydrophobic material to pulling, pushing and compression reduces the possibility of IOL damage¹².

UD613 is a hydrophilic acrylic IOL with a high water content (25%) with a hydrophobic surface and consists of one-piece optics and haptics. It is aspherical and has a modified “C” shaped haptics and is applied into the eye with a disposable plastic implantation system and a suitable disposable foldable cartridge¹³. In this system, the IOL is placed in the cartridge, then the cartridge flaps are closed and the IOL is folded. While the cartridge flaps are closed, the haptics or optical cartridge can remain between the flaps or the haptics may get stuck between the soft injector plunger and the cartridge while the IOL is injected into the eye. The high water content soft biomaterial structure of hydrophilic acrylic IOLs is also considered as another reason that increases the possibility of damage to the optic and haptics during folding and implantation^4,14. In this study, optic damage was observed in 1 of the disintegrated lenses, while haptic damage developed in all of the others. According to our observations, the compression of the haptic between the plunger and the lumen of the cartridge caused damage during the closure of the cartridge after the IOL was placed in the cartridge or while it was pushed forward by the plunger in the cartridge lumen. If the IOL pushed by the plunger in the cartridge lumen is too thin or thick, that is, it has a very high or low power, it may cause difficulties in pushing the IOL forward. Thick IOLs can get stuck at the exit of the cartridge lumen; thin ones can remain between the piston and the lumen⁴. The very thin optical and haptic structures of the very low power (0.00 and -1.00 D) 2 IOLs in Table 2 may be the cause of their damage.

IOLs of different manufacturers are implanted into the eye with different cartridge and implantation systems designed for them. IOLs to be used for the first time may be damaged while being placed in the cartridge and eye during the learning process^5,6,14. In our study, 2 of the hydrophobic surfaced high water content acrylic IOLs were damaged during the learning process. In the other group IOLs, the hydrophobic acrylic was not damaged during this process. Our observations suggest that features related to the cartridge and implantation system used, as well as experience, may also cause IOL damage.

Indication for IOL explantations are IOL damage, malposition, miscalculation of power and performance failure, opacification or staining. While damage rarely develops in one-piece acrylic IOLs, breakage can be seen mostly in the optic-haptic junction of three-piece IOLs^4,6,15. Mamalis et al.¹⁴ evaluated explantations and re-implantations, which they compiled from studies published until 2003, in terms of almost all types of IOLs currently in widespread use until that day. They also compared the damage-related change rate in one-piece hydrophobic acrylic IOLs with haptics changes due to other complications and found 7.5%. Other complications that cause IOL change are opacification, discoloration, incorrect lens power, dislocation, retinal surgery, decentration and glare. In one-piece hydrophilic acrylic IOLs with haptics, it was found that the change was mostly due to discoloration/opacification (70%). In the survey update study conducted by the same colleagues in 2007, no damaged lenses were reported in one-piece hydrophobic acrylic IOLs. They found that there was no notification of damaged lenses in one-piece hydrophilic acrylic IOLs, and the ratio of discoloration/opacification rate to other explantations this time was 60%. It was reported in the 2007 survey that the use rate of one-piece haptic hydrophobic acrylic IOLs increased compared to other material and design lenses, but no damaged lenses were seen. The effect of reducing the damage is the elimination of the imperfectness in implantation systems and cartridge technology, and the increase in the one-piece hydrophobic acrylic with haptics IOL using experience^14,15.

There are studies reporting that the choice of viscoelastic device used while placing the IOL in the cartridge causes IOL damage⁶. Insufficient viscoelastic substance into the cartridge or keeping the IOL in the cartridge for a long time may cause the IOL to stick to the cartridge¹⁶. Injecting a viscoelastic device with less pseudoplasticity into the cartridge may cause IOL damage¹⁷. In order to prevent the IOL from jamming during implantation, it is necessary to ensure sufficient wetting with a balanced salt solution and to ensure that the IOL is completely covered with viscoelastic. A slow and careful implantation while inserting into the cartridge and pushing with the injector plunger will help maintain IOL integrity¹⁸.

Various techniques have been described for the removal of the damaged IOL^19-23. The removal of the IOL can be performed by widening the main corneal incision or by dividing the IOL into many parts without expanding the incision site. After the viscoelastic device is injected into the anterior chamber and under the IOL, the IOL is divided into many parts with these techniques². In addition, the IOL can be made suitable for removal by cutting haptics and optics using ND-YAG laser²⁴. In the partial transection technique, the lens is cut in full thickness up to the center of the IOL optic, and it is held at one end with forceps and removed by rotation without expanding the corneal incision^21,25. In our study, damaged IOLs were removed using the partial transection technique.

Study Limitations

The limitations of our study were the small number of cases, retrospective examination and the difference in the number of IOLs used between the groups. The fact that more than one surgeon perform the procedures has revealed the risk of low standardization between applications. The absence of such case series in the literature made it difficult to compare the study with other possibilities. We think that a study in which we will implant the same IOL type into the eye using different implantation systems will better reveal the factor that causes damage.

TARTIŞMA

GİL’nin üretildiği materyalin özellikleri, optik ve haptik dizaynı, kullanılan implantasyon sistemi, kartuş içine uygunsuz yerleşimi, yetersiz viskoelastik kullanımı ve uygun olmayan kartuşlar fakoemülsifikasyon işlemlerinde implantasyonu sırasında GİL bütünlüğünü olumsuz etkileyebilen faktörlerdir^5,6.

Katlanabilir akrilik GİL’ler günümüzde fakoemülsifikasyon ve GİL implantasyonunda en sık kullanılan materyallerdir. Kullanımda olan tek parçalı, 3 parçalı, plate haptik veya skleral fiksasyon GİL’leri olmasına rağmen, çalışmamızda sadece tek parçalı haptikli GİL’ler kullanıldı. Akrilik GİL’leri hidrofilik akrilik, hidrofobik yüzeyli yüksek su içerikli akrilik veya hidrofobik akrilik olarak sınıflandırmak mümkündür. Hidrofobik GİL’ler %1’den daha düşük su içeriğine sahipken hidrofilik ve hidrofobik yüzeyli olanlar %18-26 arasında su içerirler^5,7.

Hidrofilik GİL’ler bir hidroksietilmetakrilat (polyHEMA) ve hidrofilik akrilik monomerden oluşur, yumuşaktırlar ve hidrofilik yapısı mükemmel esneklik sağlar. İki mm’nin altındaki korneal kesilerden yerleştirilmesi mümkündür. Katlamanın neden olduğu hasarlara karşı dayanıklıdır. Hidrofilik GİL implantasyonlarında arka kapsül kesafeti gelişme oranı yüksek olduğundan hidrofobik yüzeyli hidrofilik içerikli hibrit GİL kullanımı yaygınlaşmıştır. Bunlar çoğunlukla yüzeyde hidrofobik akrilik ile kaplanmıştır ve %25 su içeriğine sahip ultra saf akrilat monomer içerir^5,8,9.

Hidrofobik GİL’ler ise bir dizi akrilat ve metakrilat kopolimerinden oluşur. Sert polimetilmetakrilat katlanabilir ve dayanıklı bir materyale dönüştürülmüştür. Hidrofobik GİL’lere çekme ve itme kuvveti uygulanabilir; GİL’ler saniyeler içinde eski şeklini alabilir. Göz içine en az 2,2 mm’lik bir korneal kesiden yerleştirilebilir^5,7,8.

Hidrofobik akrilik bir GİL olan SA60AT’nin ön yüzeyi asferik ve bikonveks iken, arka yüzeyi 360° keskin optik kenara sahiptir. Haptikleri “C” şekilli ve optiğin devamıdır¹⁰. ZCB00 ve AAB00 diğer hidrofobik akrilik GİL’lerdir; bikonveks, ön yüzeyi asferik ve arka yüzeyi 360° optik kare kenara sahiptir¹¹. Bu GİL’lerin implantasyonu, yeniden kullanılabilen metal enjektörler için dizayn edilmiş tek kullanımlık katlanmayan kartuşlar ile yapılır. GİL kartuş oluğuna yerleştirilmekte ve metal enjektörün pistonu ilerletilerek göz içine yerleştirilmektedir. Metal iticinin kartuş oluğundan daha küçük olması ve rijid yapısı haptiği sıkıştırmadan lensi itmeye olanak sağlar⁴. Hidrofobik materyalin çekme, itme ve sıkıştırılmaya karşı dirençli yapısı lensin hasar görme olasılığını azaltır¹².

UD613 hidrofobik yüzeyli yüksek su içerikli (%25) hidrofilik akrilik bir GİL’dir ve tek parçalı optik ve haptikten oluşur. Asferiktir, modifiye “C” şekilli haptikleri vardır. Tek kullanımlık plastik implantasyon sistemi ile ona uygun tek kullanımlık katlanabilir kartuş kullanılarak göz içine uygulanır¹³. Bu sistemde GİL kartuşa yerleştirilmekte, ardından kartuş kanatları kapatılmakta ve bu sırada GİL katlanmaktadır. Kartuş kanatları kapatılırken haptikler ya da optik kartuş kanatları arasında kalabilir ya da GİL göz içine enjekte edilirken haptikler yumuşak enjektör pistonu ile kartuş arasına sıkışabilir. Hidrofilik akrilik GİL’lerin yüksek su içerikli yumuşak biyomateryal yapısı da katlama ve implantasyon sırasında optik ve haptiklerin hasarlanma ihtimalini artıran diğer bir neden olarak ele alınmıştır^4,14. Bu çalışmada bütünlüğü bozulan lenslerin 1’i dışında tümünde haptik hasarının geliştiği gözlenmiştir. Gözlemlerimize göre; GİL’nin kartuşa yerleştirildikten sonra kartuşun kapatılması esnasında ya da kartuş lümeninde piston vasıtası ile ilerletilirken haptiğin piston ile kartuş lümeni arasında sıkışması hasara neden olmuştur. Kartuş lümeni içinde piston tarafından itilen GİL’nin çok ince veya kalın olması, GİL’nin ilerleyişinde güçlük çıkarabilir. Kalın GİL’ler kartuş lümenin çıkışında sıkışabilir; ince olanlar ise piston ile lümen arasında kalabilirler¹⁴. Tablo 2’de yer alan çok düşük güçlü (0,00 ve -1,00 D) 2 GİL’nin, oldukça ince olan optik ve haptik yapıları, hasarlanmalarının nedeni olabilir.

Farklı üreticilere ait GİL’ler farklı kartuş ve atıcılar ile göz içine yerleştirilmektedir. İlk kez kullanılacak GİL’ler, öğrenme sürecinde kartuşa ve göze yerleştirilirken hasar görebilir^5,6,14. Çalışmamızda hidrofobik yüzeyli yüksek su içerikli akrilik GİL’lerden 2’si öğrenme sürecinde hasar görmüştür. Bunun yanında diğer grupta yer alan GİL’ler ise bu süreçte hasarlanmamıştır. Gözlemlerimiz, deneyimin yanında kullanılan kartuş sistemine bağlı özelliklerin de GİL hasarına neden olabileceğini düşündürmektedir.

GİL’nin hasarı, malpozisyonu, opaklaşması, renk değişimi, gücünün hatalı hesaplanması ve performans yetersizliği GİL değişim endikasyonlarındandır. Tek parçalı akrilik GİL’lerde hasar nadiren gelişirken üç parçalı GİL’lerin optik-haptik bileşkesinde kopma görülebilmektedir^4,6,15. Mamalis ve ark.¹⁴, 2003 yılına kadar yayınlanan çalışmalardan derledikleri eksplantasyonları ve re-implantasyonları o ana kadar yaygın kullanımda olan hemen hemen tüm GİL türleri açısından değerlendirmişlerdir. Ayrıca tek parça hidrofobik akrilik GİL’lerde hasara bağlı değişim oranını diğer komplikasyonlara bağlı haptik değişikliklerle karşılaştırmışlar ve oranı %7,5 olarak bulmuşlardır. GİL değişikliğine neden olan diğer komplikasyonlar opaklaşma, renk değişikliği, yanlış hesaplanan lens gücü, dislokasyon, retina cerrahisi, desantralizasyon ve kamaşma olarak belirlenmiştir. Haptikli tek parça hidrofilik akrilik GİL’lerde değişimin çoğunlukla renk değişikliği-opaklaşma nedeniyle olduğu tespit edilmiştir (%70). Aynı meslektaşlar tarafından 2007 yılında yapılan güncelleme çalışmasında, tek parça hidrofobik akrilik GİL’lerde lens hasarı bildirilmemiştir. Tek parça hidrofilik akrilik GİL’lerde de lens hasarına dair herhangi bir bildirim olmadığını ve bu sefer renk bozulması/opaklaşma oranının diğer eksplantasyonlara oranının %60 olduğunu bulmuşlardır. 2007 çalışmasında, tek parça haptik hidrofobik akrilik GİL’lerin kullanım oranının diğer materyal ve tasarım lenslerine göre artmasına rağmen herhangi bir hasarlı lens görülmediğini bildirmişlerdir. Görülen GİL hasarındaki azalmanın etkisi, implantasyon sistemlerindeki ve kartuş teknolojisindeki kusurların giderilmesi ve tek parça hidrofobik akrilik GİL’nin kullanım deneyiminin artmasıdır^14,15.

GİL’yi kartuş içerisine yerleştirirken kullanılan viskoelastik seçiminin GİL’nin bütünlüğünün bozulmasında etkili olduğunu bildiren çalışmalar vardır⁶. Kartuş içine yetersiz viskoleastik konulması ya da GİL’nin kartuş içinde uzun süre bekletilmesi, GİL’nin kartuşa yapışmasına neden olabilmektedir¹⁶. Kartuşa psödoplastisitesi düşük viskoelastik uygulanması GİL hasarına neden olabilmektedir¹⁷. İmplantasyon sırasında GİL’nin sıkışmasını önlemek için hem dengeli tuz çözeltisi ile yeterli ıslanma sağlamak hem de viskoelastikle kaplı olduğundan emin olmak gereklidir. Kartuşa yerleştirirken ve enjektörle iterken yavaş ve gözlemleyerek yapılan bir implantasyon GİL bütünlüğünü korumaya yardımcı olacaktır¹⁸.

Hasarlı GİL’nin çıkartılması için çeşitli teknikler tanımlanmıştır^19-23. GİL’nin çıkartılması ana korneal kesinin genişletilmesiyle veya kesi yerini genişletmeden GİL’nin birçok parçaya bölünmesiyle gerçekleştirilebilir. Ön kamaraya ve GİL’nin altına viskoelastik madde enjekte edildikten sonra bu tekniklerle GİL birçok parçaya bölünür². Bunun dışında haptikler ve optik ND-YAG lazer ile kesilerek GİL çıkartılmaya uygun hale getirilebilir²⁴. Parsiyel transeksiyon tekniğinde, GİL optiğinin merkezine kadar tam kat kesilir, forseps ile bir ucu kornea dışına çıkartılıp rotasyon ile korneal kesi genişletilmeden çıkartılabilir^21,25. Çalışmamızda hasarlı GİL’ler parsiyel transeksiyon tekniği kullanılarak çıkarılmıştır.

Çalışmanın Kısıtlılıkları

Olgu sayısının az olması, geriye dönük olarak inceleme yapılması ve kullanılan GİL sayılarının gruplar arasında farklılık göstermesi çalışmamızın eksik yönleri idi. Birden fazla cerrahın gerçekleştirdiği cerrahi prosedürlerde standardizasyonun düşeceği de bir gerçektir. Literatürde bu şekilde yapılmış olgu serilerinin olmayışı çalışmamızı diğer olasılıklarla karşılaştırmamızı güçleştirmiştir. Aynı GİL türünü farklı implantasyon sistemleri kullanarak göz içine yerleştireceğimiz bir çalışmanın, hasar gelişimine neden olan faktörü daha iyi ortaya çıkaracağını düşünmekteyiz.

CONCLUSION

Today, there are many IOLs and their implantation systems made by different manufacturers with different materials and designs. The structural features of the hydrophobic surfaced high water content IOLs’ cartridge and implantation system, which may have difficulties in the learning process, may cause damage to the IOL during implantation. For a problem-free implantation, we should be slow and careful during the period from inserting the IOL into the cartridge to pushing it forward into the capsule using the plunger.